ABSTRACT The effect of laser surface treatment for generation of corrosion resistant coatings on 1045 steel has been studied . Various ways of surface alloying have been investigated by using continuous CO2 laser beam : i ) irradiation ...
ABSTRACT The effect of laser surface treatment for generation of corrosion resistant coatings on 1045 steel has been studied . Various ways of surface alloying have been investigated by using continuous CO2 laser beam : i ) irradiation ...
Page 283
... laser treatment . By producing changes in the structure of surface layers , laser beam irradiation can , in principle , affect various structure sensitive properties , including corrosion resistance . A greater possibility is , however ...
... laser treatment . By producing changes in the structure of surface layers , laser beam irradiation can , in principle , affect various structure sensitive properties , including corrosion resistance . A greater possibility is , however ...
Page 319
... laser - treated specimen of Cr- plated 1045 steel ( Fig . 27d ) exhibit only pitting corrosion , random in the case of 304 steel and associated with the direction of laser beam passes in the case of Cr - plated specimen . ( In addition ...
... laser - treated specimen of Cr- plated 1045 steel ( Fig . 27d ) exhibit only pitting corrosion , random in the case of 304 steel and associated with the direction of laser beam passes in the case of Cr - plated specimen . ( In addition ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
36 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM austenitic behaviour biofilm biofouling carbon steel cathodic protection Chemical Process Industries chloride chromate chromium coating concentration copper corrosion control Corrosion Engineers corrosion inhibitors corrosion potential corrosion rate corrosion resistance Corrosion Reviews corrosion testing cost crevice corrosion current density decrease developed EDTA effect electrochemical electrode electrolyte electroplated equipment evaluation experimental Figure fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchangers heat flux heat transfer surface impedance included increase inhibition inhibitor ions iron oxide laboratory laser layer measurements mechanical melt zone method Michael Schorr NACE nickel nucleation oxygen paints paper particles phosphoric acid pitting plant plating polarization curves polarization resistance polymer pores porosity prediction present problems rate of iron scan specimen stainless steel substrate sulfuric acid Table techniques Technology temperature thickness tinplate tubes velocity W/mē welding zinc