2. EXPERIMENTAL PROCEDURE The apparatus used in this work consisted of a four neck glass flask and a condenser ( Figure 1 ) . All the experiments were conducted at boiling water conditions and atmospheric pressure . The heat source was ...
2. EXPERIMENTAL PROCEDURE The apparatus used in this work consisted of a four neck glass flask and a condenser ( Figure 1 ) . All the experiments were conducted at boiling water conditions and atmospheric pressure . The heat source was ...
Page 142
... experimental data concerning the weight loss and the electrochemical measurements as a function of the test conditions . 5.1 . Data storage In the field of corrosion and its inhibition , the storage of experimental data on files is a ...
... experimental data concerning the weight loss and the electrochemical measurements as a function of the test conditions . 5.1 . Data storage In the field of corrosion and its inhibition , the storage of experimental data on files is a ...
Page 150
... experimental polarization resistance value , R , is given by the equation / 20 / Rpe = R12 - RS , p ' where S is the exposed surface area of the working electrode . ( 2 ) Corrosion rate monitoring by the technique based on low frequency ...
... experimental polarization resistance value , R , is given by the equation / 20 / Rpe = R12 - RS , p ' where S is the exposed surface area of the working electrode . ( 2 ) Corrosion rate monitoring by the technique based on low frequency ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/mē zinc zinc powder zinc-ethyl silicate paints