Corrosion Reviews, Volumes 10-11Scientific Publications Division, Freund Publishing House, 1992 |
From inside the book
Results 1-3 of 82
Page 140
... determined by the eriochrome black T method / 15 / using a standard zinc chloride solution . Titration was necessary because the EDTA content of the commercial product varies from 95 % to 98 % and it is not easy to determine the exact ...
... determined by the eriochrome black T method / 15 / using a standard zinc chloride solution . Titration was necessary because the EDTA content of the commercial product varies from 95 % to 98 % and it is not easy to determine the exact ...
Page 67
... determined by contact angle measurements , with series of liquids with known surface tensions , by a least square ... determination of the surface tensions of magnetite and copper , and the surface tension values obtained by Chibowski ...
... determined by contact angle measurements , with series of liquids with known surface tensions , by a least square ... determination of the surface tensions of magnetite and copper , and the surface tension values obtained by Chibowski ...
Page 91
... determined potentiostatically in natural seawater at +500 mV SCE and at temperatures up to 70 ° C . SAF 2507 was corrosion resistant in all environments , while 254 SMO was attacked at 70 ° C . SINTEF , Norway The propagation rates of ...
... determined potentiostatically in natural seawater at +500 mV SCE and at temperatures up to 70 ° C . SAF 2507 was corrosion resistant in all environments , while 254 SMO was attacked at 70 ° C . SINTEF , Norway The propagation rates of ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints