From inside the book
Results 1-3 of 73
Page 231
Current density can significantly affect the porosity . Many workers have observed that the porosity is decreased by lowering the current density / 15,18,24 ... Pulsed currents have also been found to decrease porosity / 44,50 / .
Current density can significantly affect the porosity . Many workers have observed that the porosity is decreased by lowering the current density / 15,18,24 ... Pulsed currents have also been found to decrease porosity / 44,50 / .
Page 52
The addition of oxidisers ferric or cupric ion to sulphuric acid is effective on decreasing corrosion rates ... The Huey test indicates that the corrosion rate of 3R60 Urea Grade ( UNS S31603 ) will decrease from 0.32 to 0.22 mm - year1 ...
The addition of oxidisers ferric or cupric ion to sulphuric acid is effective on decreasing corrosion rates ... The Huey test indicates that the corrosion rate of 3R60 Urea Grade ( UNS S31603 ) will decrease from 0.32 to 0.22 mm - year1 ...
Page 164
... Chloride Media 0,01M 0,02M E ( mv / SCE ) 0.05M decreases when molybdate ions are present in the chloride media . ... and for the AISI 430 Ti , the slope o is greatly modified , with a great decrease of the pit generation rate .
... Chloride Media 0,01M 0,02M E ( mv / SCE ) 0.05M decreases when molybdate ions are present in the chloride media . ... and for the AISI 430 Ti , the slope o is greatly modified , with a great decrease of the pit generation rate .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
ELECTROCHEMICAL TECHNIQUES SIMPLE TESTS | 32 |
Electrochemical Techniques Simple Tests for Complex | 34 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Copyright | |
39 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloy anodes application behaviour biofilm carbon cathodic cause changes chemical chromate chromium coating complex concentration containing copper corrosion rate curves decrease dependent deposition determination developed edition effect electrochemical electrode engineering equipment evaluation example experimental experiments exposed Figure flow formation fouling frequency function growth heat flux heat transfer higher important included increase industrial inhibition inhibitors installations International ions iron oxide laboratory laser layer low alloy steel materials measurements mechanism metal method observed obtained operating organic paints particles passive performed plant polarization pores porosity possible potential practical prediction present problems protection published range reduce reference removal resistance Science selection shown shows solution specimen stainless steel substrate surface Table techniques Technology temperature thickness treatment volume zinc