... cleaning solutions containing milder organic acids which are still effective in cleaning the steam generating systems and in recovering the initial heat transfer efficiency . This approach has proved to be very promising and , from the ...
... cleaning solutions containing milder organic acids which are still effective in cleaning the steam generating systems and in recovering the initial heat transfer efficiency . This approach has proved to be very promising and , from the ...
Page 134
... cleaning solution / 7,8 / is quite understandable considering that , unlike inorganic acids containing halides , EDTA does not have the tendency to induce the undesired and dangerous phenomenon of stress corrosion cracking of stainless ...
... cleaning solution / 7,8 / is quite understandable considering that , unlike inorganic acids containing halides , EDTA does not have the tendency to induce the undesired and dangerous phenomenon of stress corrosion cracking of stainless ...
Page 135
... cleaning . After examining the practical aspects of this operation organically , the author describes the procedures to be adopted , tackles the problem of the disposal of exhausted solutions and compares the economic advantages and ...
... cleaning . After examining the practical aspects of this operation organically , the author describes the procedures to be adopted , tackles the problem of the disposal of exhausted solutions and compares the economic advantages and ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints