Corrosion Reviews, Volumes 10-11Scientific Publications Division, Freund Publishing House, 1992 |
From inside the book
Results 1-3 of 73
Page 298
... chromium , have no effect on the structure of the melt zone . In chromium coated specimens ( Fig . 13 ) the melt zone is characterized by a finer structure with less pronounced dendrite pattern . Another peculiar feature of this ...
... chromium , have no effect on the structure of the melt zone . In chromium coated specimens ( Fig . 13 ) the melt zone is characterized by a finer structure with less pronounced dendrite pattern . Another peculiar feature of this ...
Page 300
... chromium was found in the melt zone and HAZ with no chromium outside the laser affected region . However , in the cross- section sample no chromium was found within the melt zone , either . It seems that chromium determination by Auger ...
... chromium was found in the melt zone and HAZ with no chromium outside the laser affected region . However , in the cross- section sample no chromium was found within the melt zone , either . It seems that chromium determination by Auger ...
Page 302
... chromium or manganese phosphate ) in comparison with the the uncoated specimens . 4.4 . Irradiation of Chromium and Chromium - Nickel Electroplated Coatings The use of painted coatings , including the chromium one , does not produce an ...
... chromium or manganese phosphate ) in comparison with the the uncoated specimens . 4.4 . Irradiation of Chromium and Chromium - Nickel Electroplated Coatings The use of painted coatings , including the chromium one , does not produce an ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints