Eventually , however , the internal stresses cause the coating to crack causing the porosity to increase again ( Figure 8 ) . This type of behaviour is perhaps best known in high temperature oxidation when , due to external effects ...
Eventually , however , the internal stresses cause the coating to crack causing the porosity to increase again ( Figure 8 ) . This type of behaviour is perhaps best known in high temperature oxidation when , due to external effects ...
Page 234
Its Cause , Nature , Effect and Management 3.5 . The Effect of Porosity on a Coating's Performance Virtually all the problems associated with porosity in a coating can be attributed to its effect on corrosion resistance .
Its Cause , Nature , Effect and Management 3.5 . The Effect of Porosity on a Coating's Performance Virtually all the problems associated with porosity in a coating can be attributed to its effect on corrosion resistance .
Page 391
... as an unavoidable contaminant in a major liquid phase , for example , sand particles carried from the oil - bearing strata in a flow of oil from a well . When the particles are soft or weak , they will often cause negligible wear to ...
... as an unavoidable contaminant in a major liquid phase , for example , sand particles carried from the oil - bearing strata in a flow of oil from a well . When the particles are soft or weak , they will often cause negligible wear to ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
ELECTROCHEMICAL TECHNIQUES SIMPLE TESTS | 32 |
Electrochemical Techniques Simple Tests for Complex | 34 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Copyright | |
39 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloy anodes application behaviour biofilm carbon cathodic cause changes chemical chromate chromium coating complex concentration containing copper corrosion rate curves decrease dependent deposition determination developed edition effect electrochemical electrode engineering equipment evaluation example experimental experiments exposed Figure flow formation fouling frequency function growth heat flux heat transfer higher important included increase industrial inhibition inhibitors installations International ions iron oxide laboratory laser layer low alloy steel materials measurements mechanism metal method observed obtained operating organic paints particles passive performed plant polarization pores porosity possible potential practical prediction present problems protection published range reduce reference removal resistance Science selection shown shows solution specimen stainless steel substrate surface Table techniques Technology temperature thickness treatment volume zinc