Corrosion Reviews, Volumes 10-11Scientific Publications Division, Freund Publishing House, 1992 |
From inside the book
Results 1-3 of 85
Page 42
... carbon was found to pit . Polarization scans generated in the fluid not in contact with the carbon showed a dis- tinct pitting potential . The potential of carbon was found to be several hundred millivolts greater ( more noble ) than ...
... carbon was found to pit . Polarization scans generated in the fluid not in contact with the carbon showed a dis- tinct pitting potential . The potential of carbon was found to be several hundred millivolts greater ( more noble ) than ...
Page 301
... carbon coated specimen after surface sputtering shows that the height of carbon peak in this specimen is similar to that observed in chromium coated specimens . Quantitative determination of carbon content by the Auger method was ...
... carbon coated specimen after surface sputtering shows that the height of carbon peak in this specimen is similar to that observed in chromium coated specimens . Quantitative determination of carbon content by the Auger method was ...
Page 191
... carbon steel . Magnification X1500 . Samples of carbon and stainless steel assayed using identical experimental conditions ( 7 h incubation time - ca. 108 CFU / cm2 , 10 or 15 min contact times , 0.5 ppm ozone concentration ) showed a ...
... carbon steel . Magnification X1500 . Samples of carbon and stainless steel assayed using identical experimental conditions ( 7 h incubation time - ca. 108 CFU / cm2 , 10 or 15 min contact times , 0.5 ppm ozone concentration ) showed a ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints