Corrosion Reviews, Volumes 10-11Scientific Publications Division, Freund Publishing House, 1992 |
From inside the book
Results 1-3 of 42
Page 2
... biofilm thickness . The solid surface condition affects the attachment and growth of biofilms . Rough surfaces tend to encourage the retention of deposits . Some specially designed coatings appear to reduce the incidence of biofilm ...
... biofilm thickness . The solid surface condition affects the attachment and growth of biofilms . Rough surfaces tend to encourage the retention of deposits . Some specially designed coatings appear to reduce the incidence of biofilm ...
Page 8
... biofilm biofilm thickness under otherwise otherwise similar experimental conditions . The work was extended by Bott and Gunatilake / 12 / who showed something like a three - fold increase in biofilm thickness as the C : N ratio ...
... biofilm biofilm thickness under otherwise otherwise similar experimental conditions . The work was extended by Bott and Gunatilake / 12 / who showed something like a three - fold increase in biofilm thickness as the C : N ratio ...
Page 19
... biofilm the more resistant it is to the effects of ozone penetration . Over a period of time it is anticipated that the biofilm will become less " open " in structure , as the daughter cells from reproduction gradually fill the voids in ...
... biofilm the more resistant it is to the effects of ozone penetration . Over a period of time it is anticipated that the biofilm will become less " open " in structure , as the daughter cells from reproduction gradually fill the voids in ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints