where AfA is the area fraction of the anodic fraction or substrate when AfA + Afc 1. Afc is the area fraction of the cathodic fraction or coating . i is the exchange current density of the substrate , b , the anodic Tafel slope of the ...
where AfA is the area fraction of the anodic fraction or substrate when AfA + Afc 1. Afc is the area fraction of the cathodic fraction or coating . i is the exchange current density of the substrate , b , the anodic Tafel slope of the ...
Page 264
An alternative explanation for the pore resistance test was proposed by Morrissey / 148 / . He thought that " the initial linear slopes of the anodic polarisation curves of basis metal specimens coated with ...
An alternative explanation for the pore resistance test was proposed by Morrissey / 148 / . He thought that " the initial linear slopes of the anodic polarisation curves of basis metal specimens coated with ...
Page 269
20 : Porosity measurements on matte unpassivated tinplate , a comparison of the corrosion potential and polarisation conductance results / 145 / . with those from the cathodic corrosion current method and the anodic method ( Table V ) .
20 : Porosity measurements on matte unpassivated tinplate , a comparison of the corrosion potential and polarisation conductance results / 145 / . with those from the cathodic corrosion current method and the anodic method ( Table V ) .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
ELECTROCHEMICAL TECHNIQUES SIMPLE TESTS | 32 |
Electrochemical Techniques Simple Tests for Complex | 34 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Copyright | |
39 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloy anodes application behaviour biofilm carbon cathodic cause changes chemical chromate chromium coating complex concentration containing copper corrosion rate curves decrease dependent deposition determination developed edition effect electrochemical electrode engineering equipment evaluation example experimental experiments exposed Figure flow formation fouling frequency function growth heat flux heat transfer higher important included increase industrial inhibition inhibitors installations International ions iron oxide laboratory laser layer low alloy steel materials measurements mechanism metal method observed obtained operating organic paints particles passive performed plant polarization pores porosity possible potential practical prediction present problems protection published range reduce reference removal resistance Science selection shown shows solution specimen stainless steel substrate surface Table techniques Technology temperature thickness treatment volume zinc