Corrosion Reviews, Volumes 10-11Scientific Publications Division, Freund Publishing House, 1992 |
From inside the book
Results 1-3 of 89
Page 36
... acid / 14 / . When the waste stream contained this acid at an activity of 0.04 , the corrosion rate of steel was found to be of the order of 1 cm / yr in laboratory measurements at a pH of 8. Ac- celerated corrosion rates were also ...
... acid / 14 / . When the waste stream contained this acid at an activity of 0.04 , the corrosion rate of steel was found to be of the order of 1 cm / yr in laboratory measurements at a pH of 8. Ac- celerated corrosion rates were also ...
Page 378
... acid production , and he has worked in a wide variety of phosphoric acid programs in 34 countries over a 35 - year period . He studied chemical engineering at the Ecole Nationale Supérieure de Chimie de Strasbourg , France . This book ...
... acid production , and he has worked in a wide variety of phosphoric acid programs in 34 countries over a 35 - year period . He studied chemical engineering at the Ecole Nationale Supérieure de Chimie de Strasbourg , France . This book ...
Page 51
... acid Proposed values in 93 % aerated acid 22C5Ni3Mo in 10 % deaerated acid 20C18Ni6Mo in 10 % deaerated acid Proposed values in 10 % deaerated acid 133 0.5- 45 50 55 60 65 70 75 80 Temperature ( ° C ) 85 90 95 100 105 Fig . 10 Effect of ...
... acid Proposed values in 93 % aerated acid 22C5Ni3Mo in 10 % deaerated acid 20C18Ni6Mo in 10 % deaerated acid Proposed values in 10 % deaerated acid 133 0.5- 45 50 55 60 65 70 75 80 Temperature ( ° C ) 85 90 95 100 105 Fig . 10 Effect of ...
Contents
Electrochemical Techniques Simple Tests for Complex | 32 |
Cyclic Polarization Scans for Predicting Localized | 40 |
Prediction of Crevice Corrosion | 46 |
Copyright | |
35 other sections not shown
Other editions - View all
Common terms and phrases
adhesion anodic application aqueous ASTM behaviour binder biofilm biofouling carbon steel cathodic protection Chem Chemical Process Industries chromate chromium cm/sec coating concentration copper corrosion current corrosion inhibitors corrosion potential corrosion rate corrosion resistance crevice corrosion current density decrease developed EDTA Effect and Management electrochemical electrode electrolyte electroplated engineering equipment evaluation experimental Figure film fluid formation fouling growth HASTELLOY HASTELLOY alloy G-30 heat exchanger heat flux heat transfer surface impedance increase inhibition inhibitors ions iron oxide laboratory laser beam laser treated laser treatment materials measurements melt zone method Michael Schorr NACE nickel oxygen particles passive phosphate phosphoric acid pitting Plating polarisation polarization curves polarization resistance polymer pores porosity porosity tests potentiodynamic prediction present rate of iron sample silicate specimen stainless steel substrate surface layer Table techniques Technology temperature thickness tinplate topcoat velocity W/m² zinc zinc powder zinc-ethyl silicate paints