Elongation of 10" sections: 1".65, 1".72, 1.70, 1.69, 1.81, 1.90 (2.50 at fracture), 1".70. Diameter at fracture, 1".58; area, 1.96 square inches. Fracture, fibrous. No. 595. Mark on bar, S 20. Diameter, 2.01; sectional area, 3.17 square inches. Gauged length, 80". Elongation of 10" sections: 1".62 (2".34 at fracture), 1".75, 1".82, 1.81, 1.81, 1.75, 1".79. Diameter at fracture, 1".59; area, 1.99 square inches. Contraction of area, 37 per cent. Appearance of fracture fibrous, with some cinder at center. DOUBLE-REFINED WROUGHT IRON. Mark on bar, S 218. No. 596. Diameter, 2".01; sectional area, 3.17 square inches. Gauged length, 80". Elongation of 10" sections: 1".90, 1".95, 2".19, 2".08, 2".01, 2".09, 1.97, 2".13. Diameter at fracture, 1".54; area, 1.86 square inches. Contraction of area, 41 per cent. Fracture fibrous; broke outside 80" section, 2" from face of holder jaws. No. 597. Mark on bar, S 219. Diameter, 2".01; sectional area, 3.17 square inches. Elongation of 10" sections: 2".19, 2′′.26, 2′′.49, 2′′.40 (2′′.95 at fracture), 2.90, 2.44, 2".72. Diameter at fracture, 1′′.50; area, 1.77 square inches. Contraction of area, 44 per cent. Fracture fibrous, cup-shaped. No. 598. Mark on bar, S 220. Gauged length, 80". Diameter, 2".01; sectional area, 3.17 square inches. Elongation of 10" sections: 2.10, 2′′.06, 2′′.21, 27.38, 2′′.39 (3′′.35 at fracture), 2.30, 2".13. Diameter at fracture, 1".50; area, 1.77 square inches. Contraction of area, 44 per cent. Fracture fibrous, cup-shaped. |