Smoke and Gases Produced by Burning Aircraft Interior MaterialsU.S. Government Printing Office, 1969 - 27 pages |
From inside the book
Results 1-5 of 9
Page 4
... shown in appendix 4 . = A wide range of Dm values was measured . Slightly more than 15 percent of the materials produced smoke corresponding to a Dm 16 or less , for both flaming and smoldering exposures . These included materials ...
... shown in appendix 4 . = A wide range of Dm values was measured . Slightly more than 15 percent of the materials produced smoke corresponding to a Dm 16 or less , for both flaming and smoldering exposures . These included materials ...
Page 5
... Shown in HC1 Column Where Latter was not Detected Chloroprene 82 131 Chlorosulfonated PE 83 130 Silicone Rubber 63. 14 14 3,58 149 157 63 2 Modacrylic 132 29 153 28 108 5.8 107 RUGS Wool 83 17 Propylene 31 8 Modacrylic 56 148 C 64 64 153 ...
... Shown in HC1 Column Where Latter was not Detected Chloroprene 82 131 Chlorosulfonated PE 83 130 Silicone Rubber 63. 14 14 3,58 149 157 63 2 Modacrylic 132 29 153 28 108 5.8 107 RUGS Wool 83 17 Propylene 31 8 Modacrylic 56 148 C 64 64 153 ...
Page 6
... Values in Excess of Scale Values + Max . Indicated Concentrations of HF and SO2are Shown in HC1 or HCN Columns Where the Latter were not Detected 1 oz / y3.39 x 10-3 8 / cm Unit Material ( major ) Weight Sample os / yd. 6.
... Values in Excess of Scale Values + Max . Indicated Concentrations of HF and SO2are Shown in HC1 or HCN Columns Where the Latter were not Detected 1 oz / y3.39 x 10-3 8 / cm Unit Material ( major ) Weight Sample os / yd. 6.
Page 7
... Shown in HCN Column Where Latter was not Detected 1 oz / yd 3.39 x 101 8 / cm FIGURE 7. Smoke and gas concentrations for individual materials - assemblies , laminates , films . SPECIFIC OPTICAL DENSITY OF SMOKE , D 200- 150- 50-. 7.
... Shown in HCN Column Where Latter was not Detected 1 oz / yd 3.39 x 101 8 / cm FIGURE 7. Smoke and gas concentrations for individual materials - assemblies , laminates , films . SPECIFIC OPTICAL DENSITY OF SMOKE , D 200- 150- 50-. 7.
Page 8
... shown in figure 8. This figure shows the five replicate smoke curves and a tabulation of indicated gas concentrations at spe- cific times during each test . The measurement ranges were on the order of ± 20 percent for CO and HCN and ...
... shown in figure 8. This figure shows the five replicate smoke curves and a tabulation of indicated gas concentrations at spe- cific times during each test . The measurement ranges were on the order of ± 20 percent for CO and HCN and ...
Common terms and phrases
400 Maximum Smoke acetate adsorption Aircraft Interior Materials appendix asbestos Building Science Series calibration cents CHLOROPRENE cm³ cm³/min colorimetric indicator tubes colorimetric tubes components concen copolymer D₁ density of 16 density of smoke dilution Exposure Value Fabric UC film flaming and smoldering ft² gas concentrations gas detector tubes gaseous products gases Glass fiber HCl concentration inch Fabric inch Rug inch Sheet 200 indicated concentration Insulation Interrelations Between Cement Laminate limits Matte Sheet methyl methacrylate Modacrylic National Bureau Number nylon oz/yd PAPER HONEYCOMB percent Plasticized Polyamide Polyester Polyethylene terephthalate polysulfone polytetrafluoroethylene Polyvinyl Polyvinyl acetate Polyvinyl chloride Polyvinyl fluoride possible PVC precleaning layer sample Seat panels smoke accumulation smoke chamber Smoke D Smoke Measurements smoke particles smoke test chamber smoldering exposures specific ion electrode specific optical density surface area temperature terials thickness toxicological tration Typical smoke urethane urethane foam vinyl chloride volume wool
Popular passages
Page 1 - Measurements are reported of the smoke produced during both flaming and smoldering exposures on 141 aircraft interior materials. Smoke is reported in terms of specific optical density, a dimensionless attenuation coefficient which defines the photometric obscuration produced by a quantity of smoke accumulated from a specimen of given thickness and unit surface area within a chamber of unit volume. A very wide range in the maximum specific optical density was observed. For the majority of materials,...