Smoke and Gases Produced by Burning Aircraft Interior MaterialsU.S. Government Printing Office, 1969 - 27 pages |
From inside the book
Results 1-5 of 14
Page
... measurements . 2.3 . Gas analysis . 3. Test results and analysis .. 3.1 . Material identification 3.2 . Smoke measurements . 3.3 . Gas analysis . __ 4. Discussion . 5. Conclusions . 6. References 7. Appendix 1. Gas analysis . 7.1 ...
... measurements . 2.3 . Gas analysis . 3. Test results and analysis .. 3.1 . Material identification 3.2 . Smoke measurements . 3.3 . Gas analysis . __ 4. Discussion . 5. Conclusions . 6. References 7. Appendix 1. Gas analysis . 7.1 ...
Page 1
... Measurements are reported of the smoke produced during both flaming and smoldering exposures on 141 aircraft interior materials . Smoke is reported in terms of specific optical density , a dimensionless attenuation coefficient which ...
... Measurements are reported of the smoke produced during both flaming and smoldering exposures on 141 aircraft interior materials . Smoke is reported in terms of specific optical density , a dimensionless attenuation coefficient which ...
Page 2
... measured specific optical density and the level of smoke through which a light ( or lighted exit sign ) may be seen . The tests involved a thermal irradiation ex- posure of 2.5 W / cm2 ... measured over unit path length. 2 Smoke measurements.
... measured specific optical density and the level of smoke through which a light ( or lighted exit sign ) may be seen . The tests involved a thermal irradiation ex- posure of 2.5 W / cm2 ... measured over unit path length. 2 Smoke measurements.
Page 3
... measured over unit path length ( L ) , within a chamber of unit volume ( V ) , produced from a specimen of unit V V surface area ( A ) . Thus , D. = D AL AL 100 T log T = = For the test chamber , V = 18 ft3 ( 0.510 m3 ) , A 0.0456 ft2 ...
... measured over unit path length ( L ) , within a chamber of unit volume ( V ) , produced from a specimen of unit V V surface area ( A ) . Thus , D. = D AL AL 100 T log T = = For the test chamber , V = 18 ft3 ( 0.510 m3 ) , A 0.0456 ft2 ...
Page 4
... Measurements Smoke measurements are summarized in ap- pendix 3 in terms of the maximum smoke accumu- lation ( Dm ) ... measured . Slightly more than 15 percent of the materials produced smoke corresponding to a Dm 16 or less , for both ...
... Measurements Smoke measurements are summarized in ap- pendix 3 in terms of the maximum smoke accumu- lation ( Dm ) ... measured . Slightly more than 15 percent of the materials produced smoke corresponding to a Dm 16 or less , for both ...
Common terms and phrases
400 Maximum Smoke acetate adsorption Aircraft Interior Materials appendix asbestos Building Science Series calibration cents CHLOROPRENE cm³ cm³/min colorimetric indicator tubes colorimetric tubes components concen copolymer D₁ density of 16 density of smoke dilution Exposure Value Fabric UC film flaming and smoldering ft² gas concentrations gas detector tubes gaseous products gases Glass fiber HCl concentration inch Fabric inch Rug inch Sheet 200 indicated concentration Insulation Interrelations Between Cement Laminate limits Matte Sheet methyl methacrylate Modacrylic National Bureau Number nylon oz/yd PAPER HONEYCOMB percent Plasticized Polyamide Polyester Polyethylene terephthalate polysulfone polytetrafluoroethylene Polyvinyl Polyvinyl acetate Polyvinyl chloride Polyvinyl fluoride possible PVC precleaning layer sample Seat panels smoke accumulation smoke chamber Smoke D Smoke Measurements smoke particles smoke test chamber smoldering exposures specific ion electrode specific optical density surface area temperature terials thickness toxicological tration Typical smoke urethane urethane foam vinyl chloride volume wool
Popular passages
Page 1 - Measurements are reported of the smoke produced during both flaming and smoldering exposures on 141 aircraft interior materials. Smoke is reported in terms of specific optical density, a dimensionless attenuation coefficient which defines the photometric obscuration produced by a quantity of smoke accumulated from a specimen of given thickness and unit surface area within a chamber of unit volume. A very wide range in the maximum specific optical density was observed. For the majority of materials,...