Page 118
... techniques came from the production of semi - conductor devices in which field the technique offers advantages , including greater control over doping uniformity and junction depths , than diffusion . In more recent years , however ...
... techniques came from the production of semi - conductor devices in which field the technique offers advantages , including greater control over doping uniformity and junction depths , than diffusion . In more recent years , however ...
Page 31
... techniques e.g. Cr layers are formed on steel , Fe , Ni , Mo , W , Ta , and Nb by immersion in Cu melt containing Cr . Excess of Cu is then removed by acid etching . Combination with other coating techniques . Cladding Principles ...
... techniques e.g. Cr layers are formed on steel , Fe , Ni , Mo , W , Ta , and Nb by immersion in Cu melt containing Cr . Excess of Cu is then removed by acid etching . Combination with other coating techniques . Cladding Principles ...
Page 32
... technique can be used to join dissimilar metals . Limitations 1 . 2 . The size and shape of the component that can be coated is ... techniques are generally used for wear resistant applications , e.g. mining and earth - moving equipments ...
... technique can be used to join dissimilar metals . Limitations 1 . 2 . The size and shape of the component that can be coated is ... techniques are generally used for wear resistant applications , e.g. mining and earth - moving equipments ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium