Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 11
Page 302
... Sulfuric Acid Sulfuric Acid + 200 ppm Cl as NaCl Boiling Point Curve 50 mpy ( 1.27 ) 50 mpy ( 1.27 ) 150 100 5 mpy ( 0.13 ) 50 5 mpy ( 0.13 ) 20 20 30 40 50 60 70 80 90 100 CONCENTRATION , WEIGHT PERCENT Fig . 21. Corrosion of Hastelloy ...
... Sulfuric Acid Sulfuric Acid + 200 ppm Cl as NaCl Boiling Point Curve 50 mpy ( 1.27 ) 50 mpy ( 1.27 ) 150 100 5 mpy ( 0.13 ) 50 5 mpy ( 0.13 ) 20 20 30 40 50 60 70 80 90 100 CONCENTRATION , WEIGHT PERCENT Fig . 21. Corrosion of Hastelloy ...
Page 303
400 Corrosion rates in parentheses are in mm / year . 200 350 Sulfuric Acid Sulfuric Acid + 200 ppm Cl- as NaCl 150 100 5 mpy . ( 0.13 ) 50 5 mpy ( 0.13 ) 400 Corrosion rates in parentheses are in mm / year. TEMPERATURE , DEG . F 300 ...
400 Corrosion rates in parentheses are in mm / year . 200 350 Sulfuric Acid Sulfuric Acid + 200 ppm Cl- as NaCl 150 100 5 mpy . ( 0.13 ) 50 5 mpy ( 0.13 ) 400 Corrosion rates in parentheses are in mm / year. TEMPERATURE , DEG . F 300 ...
Page 304
400 Corrosion rates in parentheses are in mm / year . Sulfuric Acid 350 Sulfuric Acid 200 ppm Clas NaCl 50 mpy ( 1.27 ) - 5 mpy 150 ( 0.13 ) 5 mpy ( 0.13 ) 200 Corrosion of Hastelloy alloy B - 2 by sulfuric acid with 200 ppm chloride ...
400 Corrosion rates in parentheses are in mm / year . Sulfuric Acid 350 Sulfuric Acid 200 ppm Clas NaCl 50 mpy ( 1.27 ) - 5 mpy 150 ( 0.13 ) 5 mpy ( 0.13 ) 200 Corrosion of Hastelloy alloy B - 2 by sulfuric acid with 200 ppm chloride ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium