Page 262
Monocarboxylic acids with inhibitive properties 163 / Name of the Acid Formula Ka x 105 X Solubility mN Caprioc CHCOOH 1.4 77 Heptoic 1.3 18 CH13COOH C , H15COOH Octoic 1.41 4.8 Nonoic C2H17COOH 1.1 1.6 tative , since they were obtained ...
Monocarboxylic acids with inhibitive properties 163 / Name of the Acid Formula Ka x 105 X Solubility mN Caprioc CHCOOH 1.4 77 Heptoic 1.3 18 CH13COOH C , H15COOH Octoic 1.41 4.8 Nonoic C2H17COOH 1.1 1.6 tative , since they were obtained ...
Page 266
The inhibiting properties of these metallic cations are attributed to their ability to form insoluble or sparingly soluble hydroxides ( Table 11 ) . Table 11 . Hydroxide Solubility Product 25 ° C ( Ksp ) 3 x 10-17 6 x 10-18 Х Zn ( OH ) ...
The inhibiting properties of these metallic cations are attributed to their ability to form insoluble or sparingly soluble hydroxides ( Table 11 ) . Table 11 . Hydroxide Solubility Product 25 ° C ( Ksp ) 3 x 10-17 6 x 10-18 Х Zn ( OH ) ...
Page 24
Surface alloys independent of solid solubility and diffusivity limits can be formed . No significant dimensional changes occurs , so that the process can be applied to finished components . No adhesion problems are expected since there ...
Surface alloys independent of solid solubility and diffusivity limits can be formed . No significant dimensional changes occurs , so that the process can be applied to finished components . No adhesion problems are expected since there ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium