Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 16
Page 403
... sintered stainless steel . As a result sintered stainless steel is severely corroded in H2SO4 while a wrought plate or cast austenitic stainless steel remain passive in this environment . Improved corrosion resistance of cast metals ...
... sintered stainless steel . As a result sintered stainless steel is severely corroded in H2SO4 while a wrought plate or cast austenitic stainless steel remain passive in this environment . Improved corrosion resistance of cast metals ...
Page 404
... sintered at a temperature of 1150 ° C for 2h or 48h in vacuum lower than 1 m bar . After sintering at 1150 ° C , the specimens were water quenched . The hot pressing apparatus is described elsewhere / 3 / . The specimens obtained in ...
... sintered at a temperature of 1150 ° C for 2h or 48h in vacuum lower than 1 m bar . After sintering at 1150 ° C , the specimens were water quenched . The hot pressing apparatus is described elsewhere / 3 / . The specimens obtained in ...
Page 410
Behavior of Sintered Stainless Steel Potentiodynamic polarization curves of samples sintered for 48h tested in 1NH2SO4 solution are presented in Fig . 5. The critical and passivation current densities of the samples containing various ...
Behavior of Sintered Stainless Steel Potentiodynamic polarization curves of samples sintered for 48h tested in 1NH2SO4 solution are presented in Fig . 5. The critical and passivation current densities of the samples containing various ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium