Page 135
Figure 5 shows the decay of the anodic current density with 45 mA / cm2 3 o Unimplanted • Ti Implanted • Mo Implanted • Ni Implanted CURRENT DENSITY 1 2 3 4 TIME min Fig . 5 Anodic current decay curves for implanted and unimplanted 0.1 ...
Figure 5 shows the decay of the anodic current density with 45 mA / cm2 3 o Unimplanted • Ti Implanted • Mo Implanted • Ni Implanted CURRENT DENSITY 1 2 3 4 TIME min Fig . 5 Anodic current decay curves for implanted and unimplanted 0.1 ...
Page 229
Maximum Temperatures in Systems ( Type II Diagrams ) Figure 15 shows the data plotted using the maximum temperature in systems instead of the tube skin temperature as abscissa . Type II diagrams have the advantage of avoiding the ...
Maximum Temperatures in Systems ( Type II Diagrams ) Figure 15 shows the data plotted using the maximum temperature in systems instead of the tube skin temperature as abscissa . Type II diagrams have the advantage of avoiding the ...
Page 239
Thermodynamics of Inhibition The Pourbaix diagram for iron shows that the corrosion of iron extends over a narrower range of pH at more positive potentials than at more negative ones . Pourbaix / 3 / argues that the inhibitor polarises ...
Thermodynamics of Inhibition The Pourbaix diagram for iron shows that the corrosion of iron extends over a narrower range of pH at more positive potentials than at more negative ones . Pourbaix / 3 / argues that the inhibitor polarises ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the fields of Corrosion and Stress | 202 |
J Kolts J B C Wu?P E Manning and A I Asphahani | 280 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic applications base chemical chloride chromate coating combination composition compounds concentration considered containing Corrosion rates corrosion resistance critical curves density deposits determined effect electrochemical elements Engineering environments example expert system factor failure field Figure film growth heat higher implanted improved increase industry inhibition inhibitor ions iron knowledge layer limited materials measurements mechanism metal methods molybdate molybdenum obtained operation oxide paint passive performance pitting plating polarization possible potential present problems properties protection published Radioactive Tracer range reduced reported REVIEWS rules rust selection Services shown shows sodium solution specimens stainless steel stress corrosion cracking structure substrate surface Table techniques Technology temperature tests tube University values various zinc