Page 236
The direct application of a new type of primer directly on the rusted steel with only minor prior removal of loose rust can convert the rust to a new substrate capable of holding subsequent coats and at the same time arrest the rusting ...
The direct application of a new type of primer directly on the rusted steel with only minor prior removal of loose rust can convert the rust to a new substrate capable of holding subsequent coats and at the same time arrest the rusting ...
Page 237
Also , depending on the environment in which the rust is formed , it may entrap soluble salts such as chlorides and sulphates which in turn can act as corrosion accelerators . Any way we look at the situation , rust is a foreign ...
Also , depending on the environment in which the rust is formed , it may entrap soluble salts such as chlorides and sulphates which in turn can act as corrosion accelerators . Any way we look at the situation , rust is a foreign ...
Page 247
Paint Primers for Direct Application on Rusted Steel A – Acidic Type , One - Component Chemical Rust Converters Manufacturer Product pH Comments and Manufacturers ' Claims SFS Switzerland NOVEROX 3.0 Rust transforming emulsion ; accepts ...
Paint Primers for Direct Application on Rusted Steel A – Acidic Type , One - Component Chemical Rust Converters Manufacturer Product pH Comments and Manufacturers ' Claims SFS Switzerland NOVEROX 3.0 Rust transforming emulsion ; accepts ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the fields of Corrosion and Stress | 202 |
J Kolts J B C Wu?P E Manning and A I Asphahani | 280 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic applications base chemical chloride chromate coating combination composition compounds concentration considered containing Corrosion rates corrosion resistance critical curves density deposits determined effect electrochemical elements Engineering environments example expert system factor failure field Figure film growth heat higher implanted improved increase industry inhibition inhibitor ions iron knowledge layer limited materials measurements mechanism metal methods molybdate molybdenum obtained operation oxide paint passive performance pitting plating polarization possible potential present problems properties protection published Radioactive Tracer range reduced reported REVIEWS rules rust selection Services shown shows sodium solution specimens stainless steel stress corrosion cracking structure substrate surface Table techniques Technology temperature tests tube University values various zinc