Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 75
Page 280
... resistance of a variety of nickel - base alloys and several stainless steels is presented . Since nickel - base alloys possess much better corrosion resistance than stainless steels , more severe accelerated tests are employed to ...
... resistance of a variety of nickel - base alloys and several stainless steels is presented . Since nickel - base alloys possess much better corrosion resistance than stainless steels , more severe accelerated tests are employed to ...
Page 281
... resistance to aqueous corrosion . Tables 1 and 2 by no means cover all Fe - Ni - Cr - Mo alloys . Many have modifications such as alloy G - 3 being a low - carbon / manganese ... RESISTANCE Uniform corrosion resistance Non-oxidizing acids.
... resistance to aqueous corrosion . Tables 1 and 2 by no means cover all Fe - Ni - Cr - Mo alloys . Many have modifications such as alloy G - 3 being a low - carbon / manganese ... RESISTANCE Uniform corrosion resistance Non-oxidizing acids.
Page 403
... resistance of hot pressed stainless steel as compared to wrought stainless steel is mainly caused by the inter- connected open pores . Due to electrolyte stagnation in the intercon- nected open pores , hydrogen concentration cells were ...
... resistance of hot pressed stainless steel as compared to wrought stainless steel is mainly caused by the inter- connected open pores . Due to electrolyte stagnation in the intercon- nected open pores , hydrogen concentration cells were ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium