Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 82
Page 151
... potential such that this potential is more active than the reversible hydrogen electrode potential then passivity can be achieved by the presence of a redox system no more oxidizing than the latter . Most metals exhibit a relatively ...
... potential such that this potential is more active than the reversible hydrogen electrode potential then passivity can be achieved by the presence of a redox system no more oxidizing than the latter . Most metals exhibit a relatively ...
Page 173
... potential of the element from the point of view of enhancing the corrosion resistance of this steel in the above ... potential - current density relationships by a potentio - dynamic technique described below . The specimens were ...
... potential of the element from the point of view of enhancing the corrosion resistance of this steel in the above ... potential - current density relationships by a potentio - dynamic technique described below . The specimens were ...
Page 394
... potentials below 700 mV . Of course , potential is not the only factor dictating SCC susceptibility . However , when the potential was controlled at 500 mV , SCC of zirconium including weld metal was effectively avoided . Also , both ...
... potentials below 700 mV . Of course , potential is not the only factor dictating SCC susceptibility . However , when the potential was controlled at 500 mV , SCC of zirconium including weld metal was effectively avoided . Also , both ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium