Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 45
Page 167
... pitting of stainless steels in chloride environments Pitting is regarded as a limiting case of localized attack in which only small areas of the metal surface are attacked whilst the remainder is largely unaffected . In the laboratory ...
... pitting of stainless steels in chloride environments Pitting is regarded as a limiting case of localized attack in which only small areas of the metal surface are attacked whilst the remainder is largely unaffected . In the laboratory ...
Page 301
... pitting corrosion is expected , as in chlorine- and hypochlorite - containing alkaline solutions , the use of the Ni - Cr - Mo - type group of alloys is preferred . 3. PITTING CORROSION Pitting corrosion ( a localized - type of ...
... pitting corrosion is expected , as in chlorine- and hypochlorite - containing alkaline solutions , the use of the Ni - Cr - Mo - type group of alloys is preferred . 3. PITTING CORROSION Pitting corrosion ( a localized - type of ...
Page 307
... pitting corrosion is generally not associated with these ions . Almost any of the parameters in Table 6 may be utilized to rank materials as to their pitting resistance . Figure 26 provides such a ranking for a number of alloys by ...
... pitting corrosion is generally not associated with these ions . Almost any of the parameters in Table 6 may be utilized to rank materials as to their pitting resistance . Figure 26 provides such a ranking for a number of alloys by ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium