The tendency for corrosion of an alloy system will be determined by the extent to which the potential of the alloy has been raised . If the potential is raised into the passive region , then those alloys with good passive corrosion ...
The tendency for corrosion of an alloy system will be determined by the extent to which the potential of the alloy has been raised . If the potential is raised into the passive region , then those alloys with good passive corrosion ...
Page 301
PITTING CORROSION Pitting corrosion ( a localized - type of corrosion ) is generally characterized by the presence of passive films and the subsequent localized breakdown of passivity by aggressive ions , e.g. chloride ion .
PITTING CORROSION Pitting corrosion ( a localized - type of corrosion ) is generally characterized by the presence of passive films and the subsequent localized breakdown of passivity by aggressive ions , e.g. chloride ion .
Page 410
It should be emphasized that samples containing Ni , sintered for 48h remain passive during the immersion test and the open circuit potential was in the passive range . From the presented results and other reports / 3 , 14 / it can be ...
It should be emphasized that samples containing Ni , sintered for 48h remain passive during the immersion test and the open circuit potential was in the passive range . From the presented results and other reports / 3 , 14 / it can be ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the fields of Corrosion and Stress | 202 |
J Kolts J B C Wu?P E Manning and A I Asphahani | 280 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic applications base chemical chloride chromate coating combination composition compounds concentration considered containing Corrosion rates corrosion resistance critical curves density deposits determined effect electrochemical elements Engineering environments example expert system factor failure field Figure film growth heat higher implanted improved increase industry inhibition inhibitor ions iron knowledge layer limited materials measurements mechanism metal methods molybdate molybdenum obtained operation oxide paint passive performance pitting plating polarization possible potential present problems properties protection published Radioactive Tracer range reduced reported REVIEWS rules rust selection Services shown shows sodium solution specimens stainless steel stress corrosion cracking structure substrate surface Table techniques Technology temperature tests tube University values various zinc