Decorative coatings were obtained from acidic and alkaline solutions , the latter containing also Ag and Cu salts . Properties pertinent to decorative applications , such as wear resistance , porosity and composition , were studied .
Decorative coatings were obtained from acidic and alkaline solutions , the latter containing also Ag and Cu salts . Properties pertinent to decorative applications , such as wear resistance , porosity and composition , were studied .
Page 83
The following three studies were performed in order to evaluate the properties of deposits obtained by pulsed current ( p.c. ) as compared to those obtained by direct current ( d.c. ) . In the first work , gold deposits ( about 1.25 m ) ...
The following three studies were performed in order to evaluate the properties of deposits obtained by pulsed current ( p.c. ) as compared to those obtained by direct current ( d.c. ) . In the first work , gold deposits ( about 1.25 m ) ...
Page 404
The specimens were obtained by the following procedure : 3g of powder were hot pressed at a temperature of 650 ° C , and a pressure of 12000 psi for 5 min . After the presintering in the hot pressing process , the specimens were ...
The specimens were obtained by the following procedure : 3g of powder were hot pressed at a temperature of 650 ° C , and a pressure of 12000 psi for 5 min . After the presintering in the hot pressing process , the specimens were ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the fields of Corrosion and Stress | 202 |
J Kolts J B C Wu?P E Manning and A I Asphahani | 280 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic applications base chemical chloride chromate coating combination composition compounds concentration considered containing Corrosion rates corrosion resistance critical curves density deposits determined effect electrochemical elements Engineering environments example expert system factor failure field Figure film growth heat higher implanted improved increase industry inhibition inhibitor ions iron knowledge layer limited materials measurements mechanism metal methods molybdate molybdenum obtained operation oxide paint passive performance pitting plating polarization possible potential present problems properties protection published Radioactive Tracer range reduced reported REVIEWS rules rust selection Services shown shows sodium solution specimens stainless steel stress corrosion cracking structure substrate surface Table techniques Technology temperature tests tube University values various zinc