Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 65
Page 176
... observed to fall to around -300 to -320 mV ( sce ) which is clearly well within the range of active potentials associated with corrosion . The results are apparently contradictory to those of Tomashov and the important question is why ...
... observed to fall to around -300 to -320 mV ( sce ) which is clearly well within the range of active potentials associated with corrosion . The results are apparently contradictory to those of Tomashov and the important question is why ...
Page 209
... observed about 4 to 6 years after the start of operation . In the coolers , on the other hand , about 60 % of the SCC failures were observed within 3 years of the start of operation , but over any subsequent 3 year period the proba ...
... observed about 4 to 6 years after the start of operation . In the coolers , on the other hand , about 60 % of the SCC failures were observed within 3 years of the start of operation , but over any subsequent 3 year period the proba ...
Page 410
... observed after 48h of sintering in samples containing Ni . Lower critical and passivation current densities were observed as compared to the samples sintered for 2h , and as compared to the hot pressed sintered stainless steel . It ...
... observed after 48h of sintering in samples containing Ni . Lower critical and passivation current densities were observed as compared to the samples sintered for 2h , and as compared to the hot pressed sintered stainless steel . It ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium