Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 33
Page 245
... necessary to produce passivation ( Table 3 ) . The inhibitors produce chemical passivation ( Figure 2 ) similar to that produced by anodic polarisation , but at a more negative potential . It is believed that full passivation occurs ...
... necessary to produce passivation ( Table 3 ) . The inhibitors produce chemical passivation ( Figure 2 ) similar to that produced by anodic polarisation , but at a more negative potential . It is believed that full passivation occurs ...
Page 263
... necessary for effective inhibition depended on surface preparation , grit blasted surfaces requiring about 100 times the concentration necessary for the inhibition of abraded surfaces . They also found that the minimum concentration of ...
... necessary for effective inhibition depended on surface preparation , grit blasted surfaces requiring about 100 times the concentration necessary for the inhibition of abraded surfaces . They also found that the minimum concentration of ...
Page 107
... necessary for inhibition at 50 ° C and 60 ° C , but at higher temperatures ( up to 90 ° C ) further increase is necessary to ensure full protection / 42 / . Studies of film growth were not made and no light could be thrown on the ...
... necessary for inhibition at 50 ° C and 60 ° C , but at higher temperatures ( up to 90 ° C ) further increase is necessary to ensure full protection / 42 / . Studies of film growth were not made and no light could be thrown on the ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium