Analysis of the spectrum for the uncorroded parent metal gives a molybdenum concentration with respect to the Fe + Ni + Co continum of about 3 wt % . Analysis of the spectrum of the corroded surfaces with respect to Fe , Mo and 0 ...
Analysis of the spectrum for the uncorroded parent metal gives a molybdenum concentration with respect to the Fe + Ni + Co continum of about 3 wt % . Analysis of the spectrum of the corroded surfaces with respect to Fe , Mo and 0 ...
Page 164
of Corrosion and Stress Corrosion Cracking molybdenum . Thus , Yoshida et al / 20 / claim that the addition of 15 % Mo produces an alloy fully resistant to virtually all concentrations of sulphuric and hydrochloric acids at room ...
of Corrosion and Stress Corrosion Cracking molybdenum . Thus , Yoshida et al / 20 / claim that the addition of 15 % Mo produces an alloy fully resistant to virtually all concentrations of sulphuric and hydrochloric acids at room ...
Page 177
the molybdenum steel were observed to be about twice those formed on the plain carbon steel in the cracking range of potentials ( -650 to -670 mV sce ) . At the same time there was some indication that the molybdenum concentration in ...
the molybdenum steel were observed to be about twice those formed on the plain carbon steel in the cracking range of potentials ( -650 to -670 mV sce ) . At the same time there was some indication that the molybdenum concentration in ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the fields of Corrosion and Stress | 202 |
J Kolts J B C Wu?P E Manning and A I Asphahani | 280 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic applications base chemical chloride chromate coating combination composition compounds concentration considered containing Corrosion rates corrosion resistance critical curves density deposits determined effect electrochemical elements Engineering environments example expert system factor failure field Figure film growth heat higher implanted improved increase industry inhibition inhibitor ions iron knowledge layer limited materials measurements mechanism metal methods molybdate molybdenum obtained operation oxide paint passive performance pitting plating polarization possible potential present problems properties protection published Radioactive Tracer range reduced reported REVIEWS rules rust selection Services shown shows sodium solution specimens stainless steel stress corrosion cracking structure substrate surface Table techniques Technology temperature tests tube University values various zinc