Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 43
Page 338
... molybdate is successful in that it improves the localised corrosion resistance in the pit by forming insoluble molybdate compounds . The inhibitive film has been reported to be FeMoO4 due to the inherently lower pH and potential found ...
... molybdate is successful in that it improves the localised corrosion resistance in the pit by forming insoluble molybdate compounds . The inhibitive film has been reported to be FeMoO4 due to the inherently lower pH and potential found ...
Page 343
... molybdate containing inhibitors MOLYBDATE CONSTITUENT PATENT NUMBER Ltd AUTHOR ( S ) Sekimoto , Takejima . Endo ,. Fujita Contains molybdate e.g. solution includes 2-5 % sodium molybdate , pH 7-8.5 J. 74 30,626 Nishio , Bird Wright Chem ...
... molybdate containing inhibitors MOLYBDATE CONSTITUENT PATENT NUMBER Ltd AUTHOR ( S ) Sekimoto , Takejima . Endo ,. Fujita Contains molybdate e.g. solution includes 2-5 % sodium molybdate , pH 7-8.5 J. 74 30,626 Nishio , Bird Wright Chem ...
Page 344
... molybdate JK 77,134,644 Sodium molybdate ( 0.01-1 % ) Contains alkali metal molybdate e.g. solution including 50 ppm sodium molybdate JK 78 75,139 JKTK 78,110,934 AUTHOR ( S ) COMPANY TABLE 5 : ( Cont. Sekimoto , Takejima , Endo Nisshin ...
... molybdate JK 77,134,644 Sodium molybdate ( 0.01-1 % ) Contains alkali metal molybdate e.g. solution including 50 ppm sodium molybdate JK 78 75,139 JKTK 78,110,934 AUTHOR ( S ) COMPANY TABLE 5 : ( Cont. Sekimoto , Takejima , Endo Nisshin ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium