Page 189
An " attribute ” for the pulp and paper system is the “ type of mill ” involved . “ Values ” for this attribute are “ sulfite ” and “ kraft ” mills . Only useful and pertinent “ attributes " and " values " are used .
An " attribute ” for the pulp and paper system is the “ type of mill ” involved . “ Values ” for this attribute are “ sulfite ” and “ kraft ” mills . Only useful and pertinent “ attributes " and " values " are used .
Page 190
Field corrosion test results in sulfite mills . Field Test No. 1 2 3 4 PREVIOUS MATERIAL 317L 316L 625 / 316L 625 SERVICE LIFE ( yrs ) 2 1/2 Unknown 3-1 / 2 FERRALIUM is a registered trademark of Langley Alloys Ltd. 1 1 ! Table 3.
Field corrosion test results in sulfite mills . Field Test No. 1 2 3 4 PREVIOUS MATERIAL 317L 316L 625 / 316L 625 SERVICE LIFE ( yrs ) 2 1/2 Unknown 3-1 / 2 FERRALIUM is a registered trademark of Langley Alloys Ltd. 1 1 ! Table 3.
Page 195
IMPLEMENTATION The expert system for the pulp and paper mill processes applications was tested and verified by corrosion experts within the company . The system was judged to provide the correct suggestions on materials of construction ...
IMPLEMENTATION The expert system for the pulp and paper mill processes applications was tested and verified by corrosion experts within the company . The system was judged to provide the correct suggestions on materials of construction ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the fields of Corrosion and Stress | 202 |
J Kolts J B C Wu?P E Manning and A I Asphahani | 280 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
adsorbed alloys aluminium anodic applications Artificial Intelligence Boiling Point Curve brazing cathodic chemical engineering chloride ion chromate composition compounds concentration containing conversion coatings Corrosion Control corrosion fatigue Corrosion of Hastelloy Corrosion rates corrosion resistance Corrosion Services crack growth current density deposits effect electrochemical electron environments example expert system films formed Hastelloy Hastelloy alloy heat exchangers increase industry inhibition inhibitor ion implantation iron Israel knowledge base layer materials Metallurgy methods mild steel mm/year molybdate e.g. molybdenum molybdenum blue molybdic acid NaCl NC NC NC nickel-base alloys oxide oxide film oxygen passive phosphate pitting corrosion plating polarization potential problems Prof properties protection rates in parentheses reduced REVIEWS rules rust sodium molybdate soldering solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted water path WEIGHT PERCENT Fig welding zinc