Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 3
Page 232
installed to test different configurations . With a delivery of about 5 m3 / h a pump ensures a continuous change of water inside the box . Some of the results obtained are given in Fig 9 which displays isopotential curves of the ...
installed to test different configurations . With a delivery of about 5 m3 / h a pump ensures a continuous change of water inside the box . Some of the results obtained are given in Fig 9 which displays isopotential curves of the ...
Page 340
... Sanicro 28 , were also installed in the plant in parallel service with the long lived impeller . It may be noted that 15 1 . 5 . 3 = 5 WPA industrial 340 Vol . 7 , No. 4 , 1987 Development , Testing and Use of a New Erosion - Corrosion.
... Sanicro 28 , were also installed in the plant in parallel service with the long lived impeller . It may be noted that 15 1 . 5 . 3 = 5 WPA industrial 340 Vol . 7 , No. 4 , 1987 Development , Testing and Use of a New Erosion - Corrosion.
Page 345
... INSTALLED IN THE PLANT FROM 7/84 TO 10/85 Impellers 6 units 71 mos CED Impellers 13 units 25 ± 15 days CED Alloy composition outside stated ratio limits * Further details in text Resistant , Austenitic Stainless Steel responsible for a ...
... INSTALLED IN THE PLANT FROM 7/84 TO 10/85 Impellers 6 units 71 mos CED Impellers 13 units 25 ± 15 days CED Alloy composition outside stated ratio limits * Further details in text Resistant , Austenitic Stainless Steel responsible for a ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium