Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 9
Page 360
... initiation increased . 1. INTRODUCTION A model SO2 scrubber at the LaQue Center for Corrosion Technology , Inc. ( LCCT ) has been used to characterize the corrosion behavior of austenitic stainless steels and nickel base alloys exposed ...
... initiation increased . 1. INTRODUCTION A model SO2 scrubber at the LaQue Center for Corrosion Technology , Inc. ( LCCT ) has been used to characterize the corrosion behavior of austenitic stainless steels and nickel base alloys exposed ...
Page 376
... initiation , i.e. , the total crevice area attacked , increased with increasing exposure time . As seen in Figure 8 , alloys 625 and C - 276 exhibited good corrosion resistance . Alloys 904L , SS317LM , SS316 , and alloy G , listed in ...
... initiation , i.e. , the total crevice area attacked , increased with increasing exposure time . As seen in Figure 8 , alloys 625 and C - 276 exhibited good corrosion resistance . Alloys 904L , SS317LM , SS316 , and alloy G , listed in ...
Page 389
... initiation of cracks . Results of U - bend tests of a zirconium - 1.5 % tin alloy in 90 % HNO3 showed that surface scratches serve as sites for crack initiation and lowered time - to - failure / 9 / . Improved surface quality will ...
... initiation of cracks . Results of U - bend tests of a zirconium - 1.5 % tin alloy in 90 % HNO3 showed that surface scratches serve as sites for crack initiation and lowered time - to - failure / 9 / . Improved surface quality will ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium