Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 91
Page 239
... inhibitor polarises the iron anodically , shifting it to the passive region . At the same time the inhibitor is reduced and the solid reduction products deposit on the weak points of the film improving its protective effect . To predict ...
... inhibitor polarises the iron anodically , shifting it to the passive region . At the same time the inhibitor is reduced and the solid reduction products deposit on the weak points of the film improving its protective effect . To predict ...
Page 248
... inhibitor and aggressive ions , and defined a critical ratio as the value for [ inhibitor ions ] / [ aggressive ions ] ... Inhibitors and Inhibition Mechanisms for.
... inhibitor and aggressive ions , and defined a critical ratio as the value for [ inhibitor ions ] / [ aggressive ions ] ... Inhibitors and Inhibition Mechanisms for.
Page 274
... inhibitors / 88 / . Inhibitor 75 ppm aminophosphonate 15 ppm NO2 50 ppm zinc - chromate 500 ppm nitrite 100 ppm zinc - phosphonate Corrosion rate of mild steel ( mdd ) 1.7 10.8 17.5 5.8 However , the formulation can be used successfully ...
... inhibitors / 88 / . Inhibitor 75 ppm aminophosphonate 15 ppm NO2 50 ppm zinc - chromate 500 ppm nitrite 100 ppm zinc - phosphonate Corrosion rate of mild steel ( mdd ) 1.7 10.8 17.5 5.8 However , the formulation can be used successfully ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium