Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 80
Page 254
Mild Steel in Cooling Water Systems Their rate of reversion increases with increasing temperature and decreasing pH ... increased by complex ion formation ( meta- and polyphosphates give complex ions with zinc , magnesium and calcium ) ...
Mild Steel in Cooling Water Systems Their rate of reversion increases with increasing temperature and decreasing pH ... increased by complex ion formation ( meta- and polyphosphates give complex ions with zinc , magnesium and calcium ) ...
Page 325
... Increased molybdenum in alloys is beneficial for resistance in nonoxidizing acids , ( 2 ) Increased chromium in alloys is beneficial for resistance in oxidizing environments , ( 3 ) Increased nickel in alloys is beneficial for ...
... Increased molybdenum in alloys is beneficial for resistance in nonoxidizing acids , ( 2 ) Increased chromium in alloys is beneficial for resistance in oxidizing environments , ( 3 ) Increased nickel in alloys is beneficial for ...
Page 376
... increased with increasing environmental fluoride content . No consistent effect of flyash ( added to the slurry ) on alloy corrosion resistance was discernible . The alloys ranked as to increasing localized corrosion resistance as ...
... increased with increasing environmental fluoride content . No consistent effect of flyash ( added to the slurry ) on alloy corrosion resistance was discernible . The alloys ranked as to increasing localized corrosion resistance as ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium