Page 123
The existence of large compressive stresses induced by implantation was first demonstrated by Eer Nisse / 97 , whilst later , Hartley / 10 / showed that , in annealed steels implanted with high doses of nitrogen and argon , stresses in ...
The existence of large compressive stresses induced by implantation was first demonstrated by Eer Nisse / 97 , whilst later , Hartley / 10 / showed that , in annealed steels implanted with high doses of nitrogen and argon , stresses in ...
Page 136
of Corrosion and Stress Corrosion Cracking 15 ( a ) MA / cm2 • Unimplanted • TI Implanted • Mo Implanted • NI Implanted * Ar Implanted 10H CURRENT DENSITY 2 3 5 6 TIME min 15 ( b ) MA / cm2 o Unimplanted • 1.36 % TI Steel 4 2.2 % Mo ...
of Corrosion and Stress Corrosion Cracking 15 ( a ) MA / cm2 • Unimplanted • TI Implanted • Mo Implanted • NI Implanted * Ar Implanted 10H CURRENT DENSITY 2 3 5 6 TIME min 15 ( b ) MA / cm2 o Unimplanted • 1.36 % TI Steel 4 2.2 % Mo ...
Page 164
If the latter is the predominating factor then molybdenum introduced by implantation is unlikely to have any effect , but if the molybdenum is beneficial because of its influence on filming properties the implanted molybdenum should ...
If the latter is the predominating factor then molybdenum introduced by implantation is unlikely to have any effect , but if the molybdenum is beneficial because of its influence on filming properties the implanted molybdenum should ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the fields of Corrosion and Stress | 202 |
J Kolts J B C Wu?P E Manning and A I Asphahani | 280 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic applications base chemical chloride chromate coating combination composition compounds concentration considered containing Corrosion rates corrosion resistance critical curves density deposits determined effect electrochemical elements Engineering environments example expert system factor failure field Figure film growth heat higher implanted improved increase industry inhibition inhibitor ions iron knowledge layer limited materials measurements mechanism metal methods molybdate molybdenum obtained operation oxide paint passive performance pitting plating polarization possible potential present problems properties protection published Radioactive Tracer range reduced reported REVIEWS rules rust selection Services shown shows sodium solution specimens stainless steel stress corrosion cracking structure substrate surface Table techniques Technology temperature tests tube University values various zinc