ABSTRACT In 1976 , the Plant Materials Engineering Committee of the Society of Chemical Engineers , Japan , performed a questionnaire examination concerned with stress corrosion cracking ( SCC ) of heat exchangers made of stainless ...
ABSTRACT In 1976 , the Plant Materials Engineering Committee of the Society of Chemical Engineers , Japan , performed a questionnaire examination concerned with stress corrosion cracking ( SCC ) of heat exchangers made of stainless ...
Page 209
TABLE 1 - Continued Alteration of tube to tube sheet joints , Alteration of water or vapour path , Alteration of heat exchanger structure , Cathodic protection , Water treatment ( Alteration of water quality etc. ) ...
TABLE 1 - Continued Alteration of tube to tube sheet joints , Alteration of water or vapour path , Alteration of heat exchanger structure , Cathodic protection , Water treatment ( Alteration of water quality etc. ) ...
Page 234
Relating to the Stress Corrosion Cracking of Heat Exchangers Used in Japanese Chemical Plants III diagrams are reasonable for the analysis of SCC failure data for heat exchangers operated under various conditions .
Relating to the Stress Corrosion Cracking of Heat Exchangers Used in Japanese Chemical Plants III diagrams are reasonable for the analysis of SCC failure data for heat exchangers operated under various conditions .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the fields of Corrosion and Stress | 202 |
J Kolts J B C Wu?P E Manning and A I Asphahani | 280 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic applications base chemical chloride chromate coating combination composition compounds concentration considered containing Corrosion rates corrosion resistance critical curves density deposits determined effect electrochemical elements Engineering environments example expert system factor failure field Figure film growth heat higher implanted improved increase industry inhibition inhibitor ions iron knowledge layer limited materials measurements mechanism metal methods molybdate molybdenum obtained operation oxide paint passive performance pitting plating polarization possible potential present problems properties protection published Radioactive Tracer range reduced reported REVIEWS rules rust selection Services shown shows sodium solution specimens stainless steel stress corrosion cracking structure substrate surface Table techniques Technology temperature tests tube University values various zinc