... heat transfer tubes and the chloride ion concentration in the cooling / heating medium . The results were greatly affected by the positions of and the water paths of the heat exchangers . A guide to preventing SCC was obtained from the ...
... heat transfer tubes and the chloride ion concentration in the cooling / heating medium . The results were greatly affected by the positions of and the water paths of the heat exchangers . A guide to preventing SCC was obtained from the ...
Page 209
... heat exchangers which occurred SCC ( ) ( Cracked heat exchangers / total heat exchangers ) . 1. SCC PROBABILITY CLASSIFIED BY VARIOUS ITEMS ( a ) Difference in usage as heaters or coolers Table 2 shows the probability of SCC failures in ...
... heat exchangers which occurred SCC ( ) ( Cracked heat exchangers / total heat exchangers ) . 1. SCC PROBABILITY CLASSIFIED BY VARIOUS ITEMS ( a ) Difference in usage as heaters or coolers Table 2 shows the probability of SCC failures in ...
Page 234
... heat exchangers operated under various conditions . CONCLUSIONS In Section I , the analysis of SCC probabilities for heat exchangers used as coolers showed that more than half the number of coolers that experienced SCC failures did so ...
... heat exchangers operated under various conditions . CONCLUSIONS In Section I , the analysis of SCC probabilities for heat exchangers used as coolers showed that more than half the number of coolers that experienced SCC failures did so ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium