INTRODUCTION The uses of fatigue crack growth analysis are many and varied , but the primary purpose of such an analysis , from the standpoint of Section XI of the A.S.M.E. Code is to estimate the growth which a flaw detected during ...
INTRODUCTION The uses of fatigue crack growth analysis are many and varied , but the primary purpose of such an analysis , from the standpoint of Section XI of the A.S.M.E. Code is to estimate the growth which a flaw detected during ...
Page 195
crit The fatigue crack propagation for both steels showed that the environmental enhancement of fatigue crack growth rates increases as the frequency of testing was decreased , using either sine or triangular wave forms .
crit The fatigue crack propagation for both steels showed that the environmental enhancement of fatigue crack growth rates increases as the frequency of testing was decreased , using either sine or triangular wave forms .
Page 102
Stern has also observed direct logarithmic growth of a film by electrochemical measurements on stainless steel in ferrous - ferric solutions . He has suggested that his results could also fit an inverse logarithmic growth law / 57 ) .
Stern has also observed direct logarithmic growth of a film by electrochemical measurements on stainless steel in ferrous - ferric solutions . He has suggested that his results could also fit an inverse logarithmic growth law / 57 ) .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the fields of Corrosion and Stress | 202 |
J Kolts J B C Wu?P E Manning and A I Asphahani | 280 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic applications base chemical chloride chromate coating combination composition compounds concentration considered containing Corrosion rates corrosion resistance critical curves density deposits determined effect electrochemical elements Engineering environments example expert system factor failure field Figure film growth heat higher implanted improved increase industry inhibition inhibitor ions iron knowledge layer limited materials measurements mechanism metal methods molybdate molybdenum obtained operation oxide paint passive performance pitting plating polarization possible potential present problems properties protection published Radioactive Tracer range reduced reported REVIEWS rules rust selection Services shown shows sodium solution specimens stainless steel stress corrosion cracking structure substrate surface Table techniques Technology temperature tests tube University values various zinc