... film and the extent of protection depends on the quality of the film and the ability of the inhibitor to repair defects that occur in this film . 1.2 . Films Formed on Iron and Low Carbon Steels The composition and the structure of the ...
... film and the extent of protection depends on the quality of the film and the ability of the inhibitor to repair defects that occur in this film . 1.2 . Films Formed on Iron and Low Carbon Steels The composition and the structure of the ...
Page 242
... films formed on iron in a solution of 0.1 M NaзAsO4 , pH 8.5 at open circuit potential con- sisted of iron oxide with ferric arsenate and some deposited elemental arsenic , indicating that cathodic reduction of arsenate does occur ...
... films formed on iron in a solution of 0.1 M NaзAsO4 , pH 8.5 at open circuit potential con- sisted of iron oxide with ferric arsenate and some deposited elemental arsenic , indicating that cathodic reduction of arsenate does occur ...
Page 252
Mild Steel in Cooling Water Systems and the presence of oxygen . Films formed in deaerated solutions at pH's 4.5-12.5 consist of iron phosphate with no protective ability / 45 / . If the surface has an air - formed film prior to ...
Mild Steel in Cooling Water Systems and the presence of oxygen . Films formed in deaerated solutions at pH's 4.5-12.5 consist of iron phosphate with no protective ability / 45 / . If the surface has an air - formed film prior to ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium