... Environments Oxidizing environments are generally characterized by a redox reaction where a soluble species other than H is reduced . Some common species include NO2 , Cr2O72 , MnO4 , Fe + 3 , Cu + 2 , and oxygen . The oxidizing species ...
... Environments Oxidizing environments are generally characterized by a redox reaction where a soluble species other than H is reduced . Some common species include NO2 , Cr2O72 , MnO4 , Fe + 3 , Cu + 2 , and oxygen . The oxidizing species ...
Page 310
... Environments In the absence of oxygen , all of the nickel - base alloys exhibit excellent stress corrosion cracking resistance with no failures reported in CO2 / H2S / CI environments up to 500 ° F . These alloys become susceptible to ...
... Environments In the absence of oxygen , all of the nickel - base alloys exhibit excellent stress corrosion cracking resistance with no failures reported in CO2 / H2S / CI environments up to 500 ° F . These alloys become susceptible to ...
Page 287
... Environments . Developed by National Bureau of Standards ( NBS ) . Published by NACE , P.O. Box 218340 , Houston , Texas 77218 , USA ( 1986 ) Minimum System Requirements : IBM PC , XT , AT , or compatible computers , DOS 2.0 or later ...
... Environments . Developed by National Bureau of Standards ( NBS ) . Published by NACE , P.O. Box 218340 , Houston , Texas 77218 , USA ( 1986 ) Minimum System Requirements : IBM PC , XT , AT , or compatible computers , DOS 2.0 or later ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium