Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 55
Page 168
... elements render stainless steels less susceptible to pitting corrosion is not known with any certainty . There is still no unequivocal answer to the question of whether the primary influence of alloying elements is to reduce the ...
... elements render stainless steels less susceptible to pitting corrosion is not known with any certainty . There is still no unequivocal answer to the question of whether the primary influence of alloying elements is to reduce the ...
Page 280
... elements displaying the highest stress corrosion cracking resistance . Interstitial elements play a dominant role in weld corrosion performance . 1. INTRODUCTION Today , a materials engineer has an enormous number of austenitic ...
... elements displaying the highest stress corrosion cracking resistance . Interstitial elements play a dominant role in weld corrosion performance . 1. INTRODUCTION Today , a materials engineer has an enormous number of austenitic ...
Page 314
... elements in the heat - effected zone corrosion , other elements ( e.g. , niobium ) can effect the Fe - Ni - Cr - Mo alloys ' resistance to hot cracking during welding . Three examples of the effect of alloy content on weldments are ...
... elements in the heat - effected zone corrosion , other elements ( e.g. , niobium ) can effect the Fe - Ni - Cr - Mo alloys ' resistance to hot cracking during welding . Three examples of the effect of alloy content on weldments are ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium