A comparative study of properties of Au electroplates obtained by pulsed current vs. direct current was made on thin deposits obtained from alkaline and neutral solutions . No significant differences were found in wear resistance ...
A comparative study of properties of Au electroplates obtained by pulsed current vs. direct current was made on thin deposits obtained from alkaline and neutral solutions . No significant differences were found in wear resistance ...
Page 78
The effect of the alloying elements in the deposit on its color is seen in Table 2 . TABLE 2 : Effect of alloying elements on color Cu + red Ni → white Cu + Ag + yellow Ag + green Zn → green Cd + green Most decorative deposits are ...
The effect of the alloying elements in the deposit on its color is seen in Table 2 . TABLE 2 : Effect of alloying elements on color Cu + red Ni → white Cu + Ag + yellow Ag + green Zn → green Cd + green Most decorative deposits are ...
Page 83
More homogeneous alloy deposits / 15 / . The following three studies were performed in order to evaluate the properties of deposits obtained by pulsed current ( p.c. ) as compared to those obtained by direct current ( d.c. ) .
More homogeneous alloy deposits / 15 / . The following three studies were performed in order to evaluate the properties of deposits obtained by pulsed current ( p.c. ) as compared to those obtained by direct current ( d.c. ) .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the fields of Corrosion and Stress | 202 |
J Kolts J B C Wu?P E Manning and A I Asphahani | 280 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic applications base chemical chloride chromate coating combination composition compounds concentration considered containing Corrosion rates corrosion resistance critical curves density deposits determined effect electrochemical elements Engineering environments example expert system factor failure field Figure film growth heat higher implanted improved increase industry inhibition inhibitor ions iron knowledge layer limited materials measurements mechanism metal methods molybdate molybdenum obtained operation oxide paint passive performance pitting plating polarization possible potential present problems properties protection published Radioactive Tracer range reduced reported REVIEWS rules rust selection Services shown shows sodium solution specimens stainless steel stress corrosion cracking structure substrate surface Table techniques Technology temperature tests tube University values various zinc