Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 36
Page 76
... deposits obtained by pulse plating were studied . It was found that in these , relatively thick deposits , pulse plating is advantageous . Higher plating rates and lower porosity were obtained as compared to these characteristics of ...
... deposits obtained by pulse plating were studied . It was found that in these , relatively thick deposits , pulse plating is advantageous . Higher plating rates and lower porosity were obtained as compared to these characteristics of ...
Page 78
... deposit on its color is seen in Table 2 . TABLE 2 : Effect of alloying elements on color Cu → red Ag → green Ni → white → Cu + Ag yellow Zn → green Cd → green Most decorative deposits are obtained from solutions which differ from ...
... deposit on its color is seen in Table 2 . TABLE 2 : Effect of alloying elements on color Cu → red Ag → green Ni → white → Cu + Ag yellow Zn → green Cd → green Most decorative deposits are obtained from solutions which differ from ...
Page 83
... deposits obtained by pulsed current ( p.c. ) as compared to those obtained by direct current ( d.c. ) . In the first work , gold deposits ( about 1.25 μ ) thick were deposited on brass substrates with 5 μ Ni undercoat . The solution ...
... deposits obtained by pulsed current ( p.c. ) as compared to those obtained by direct current ( d.c. ) . In the first work , gold deposits ( about 1.25 μ ) thick were deposited on brass substrates with 5 μ Ni undercoat . The solution ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium