Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 94
Page 177
... cracking in carbonate - bicarbonate and aqueous sodium chloride solutions respectively , despite the fact that high compressive stresses are known to inhibit stress corrosion cracking in many instances . The reason for this probably ...
... cracking in carbonate - bicarbonate and aqueous sodium chloride solutions respectively , despite the fact that high compressive stresses are known to inhibit stress corrosion cracking in many instances . The reason for this probably ...
Page 309
... cracking resistance than the austenitic stainless steels . Also , there are large differences among the various nickel - base alloys with regard to susceptibility to stress corrosion cracking . Generally , the beneficial effects of ...
... cracking resistance than the austenitic stainless steels . Also , there are large differences among the various nickel - base alloys with regard to susceptibility to stress corrosion cracking . Generally , the beneficial effects of ...
Page 310
... Cracking to 450 ° F 4.2 . Sour Gas Environments In the absence of oxygen , all of the nickel - base alloys exhibit excellent stress corrosion cracking resistance with no failures reported in CO2 / H2S / CI environments up to 500 ° F ...
... Cracking to 450 ° F 4.2 . Sour Gas Environments In the absence of oxygen , all of the nickel - base alloys exhibit excellent stress corrosion cracking resistance with no failures reported in CO2 / H2S / CI environments up to 500 ° F ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium