Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 35
Page 187
... crack tip is insufficient to maintain a bare surface condition , then crack growth rates will be below those predicted by the dissolution mechanism . Conversely , when the crack tip strain rate is too high , mechanical crack advancement ...
... crack tip is insufficient to maintain a bare surface condition , then crack growth rates will be below those predicted by the dissolution mechanism . Conversely , when the crack tip strain rate is too high , mechanical crack advancement ...
Page 195
... crack growth rates . A square wave or negative sawtooth loading at 0.1 Hz reduced the fatigue crack growth rate almost to the level observed in air . Triangular and positive sawtooth waveforms led to the same environmental enhancement ...
... crack growth rates . A square wave or negative sawtooth loading at 0.1 Hz reduced the fatigue crack growth rate almost to the level observed in air . Triangular and positive sawtooth waveforms led to the same environmental enhancement ...
Page 200
... crack occurs , then the calculations of crack growth must be based on corrosion fatigue and stress corrosion data : a . The data base for information on the corrosion fatigue of pressure vessel steels ( P.W.R. environments ) has been ...
... crack occurs , then the calculations of crack growth must be based on corrosion fatigue and stress corrosion data : a . The data base for information on the corrosion fatigue of pressure vessel steels ( P.W.R. environments ) has been ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium