Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 82
Page 162
... corrosion rates for the implanted material are compared with the unimplanted controls in Table 3.9 . Table 3.9 Corrosion rates of commercial purity titanium in hydro- chloric acid at two concentrations and 20 ° C . Corrosion Rate gm ...
... corrosion rates for the implanted material are compared with the unimplanted controls in Table 3.9 . Table 3.9 Corrosion rates of commercial purity titanium in hydro- chloric acid at two concentrations and 20 ° C . Corrosion Rate gm ...
Page 164
... Corrosion rate in sulphuric acid Corrosion rates of molybdenum implanted and unimplanted titanium were determined in 40 wt % sulphuric acid at ambient temperature , chosen because the work of Yoshida et al . indicated that bulk alloyed ...
... Corrosion rate in sulphuric acid Corrosion rates of molybdenum implanted and unimplanted titanium were determined in 40 wt % sulphuric acid at ambient temperature , chosen because the work of Yoshida et al . indicated that bulk alloyed ...
Page 293
... corrosion rates , which generally increase with increase in temperature . The effect of acid concentration on corrosion rate depends on the nature of the acid and its ionization in water . In general , at very high concentration ...
... corrosion rates , which generally increase with increase in temperature . The effect of acid concentration on corrosion rate depends on the nature of the acid and its ionization in water . In general , at very high concentration ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium