Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 41
Page 184
... corrosion fatigue in P.W.R. vessels . Consideration is given to the A.S.M.E. codes and mechanisms of corrosion fatigue . 1. INTRODUCTION The uses of fatigue crack growth analysis are many and varied , but the primary purpose of such an ...
... corrosion fatigue in P.W.R. vessels . Consideration is given to the A.S.M.E. codes and mechanisms of corrosion fatigue . 1. INTRODUCTION The uses of fatigue crack growth analysis are many and varied , but the primary purpose of such an ...
Page 186
... fatigue curves , as shown in Figure 1 , c , d and e . The shape of curve depends on whether or not there is a synergistic effect of the corrosive environment and the alternating stress that ... Corrosion Fatigue in Pressurized Water Reactors.
... fatigue curves , as shown in Figure 1 , c , d and e . The shape of curve depends on whether or not there is a synergistic effect of the corrosive environment and the alternating stress that ... Corrosion Fatigue in Pressurized Water Reactors.
Page 312
... CORROSION FATIGUE Corrosion fatigue , resulting from the combined action of a corrosive environment and repeated or alternate stress , adversely effects the mechanical properties of structural materials . Such a combined action ...
... CORROSION FATIGUE Corrosion fatigue , resulting from the combined action of a corrosive environment and repeated or alternate stress , adversely effects the mechanical properties of structural materials . Such a combined action ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium