Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 88
Page 405
... containing Cu at various concentrations reaches a value of about + 200mV ( SCE ) as compared to 250mV ( SCE ) for the hot pressed sintered stainless steel . Hydrogen evolution is observed at potential lower than 200mV ( SCE ) . Hydrogen ...
... containing Cu at various concentrations reaches a value of about + 200mV ( SCE ) as compared to 250mV ( SCE ) for the hot pressed sintered stainless steel . Hydrogen evolution is observed at potential lower than 200mV ( SCE ) . Hydrogen ...
Page 408
... containing Ni during the immersion test was negligible . In the first stages , the value of the open circuit potential of the samples containing 1 and 5wt % Ni are lower than + 200mV ( SCE ) . During the exposure to IN H2SO4 higher ...
... containing Ni during the immersion test was negligible . In the first stages , the value of the open circuit potential of the samples containing 1 and 5wt % Ni are lower than + 200mV ( SCE ) . During the exposure to IN H2SO4 higher ...
Page 410
... containing Ni . Lower critical and passivation current densities were observed as compared to the samples sintered for 2h , and as compared to the hot pressed sintered stainless steel . It should be emphasized that samples containing Ni ...
... containing Ni . Lower critical and passivation current densities were observed as compared to the samples sintered for 2h , and as compared to the hot pressed sintered stainless steel . It should be emphasized that samples containing Ni ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium