Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 32
Page 206
... chloride ion concentration on the basis of data obtained from the actual use situations . This diagram has been widely used in Japan , as the " Nishino Diagram " , which indicated the existence of a critical chloride ion concentration ...
... chloride ion concentration on the basis of data obtained from the actual use situations . This diagram has been widely used in Japan , as the " Nishino Diagram " , which indicated the existence of a critical chloride ion concentration ...
Page 214
... chloride ions would combine to cause SCC failure in such regions . ( g ) Chloride ion concentration in cooling water Table 8 shows the SCC probability classified by chloride ion con- centrations . The SCC probability increases with ...
... chloride ions would combine to cause SCC failure in such regions . ( g ) Chloride ion concentration in cooling water Table 8 shows the SCC probability classified by chloride ion con- centrations . The SCC probability increases with ...
Page 229
... chloride ion concentration and maximum temperature of the system . of ' vertical - out ' , because of the vapour ... chloride ions . Under this condition of exclusion , the addition of the inhibitor increases the critical tem ...
... chloride ion concentration and maximum temperature of the system . of ' vertical - out ' , because of the vapour ... chloride ions . Under this condition of exclusion , the addition of the inhibitor increases the critical tem ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 202 |
J Kolts J B C Wu P E Manning and A I Asphahani | 280 |
Copyright | |
48 other sections not shown
Other editions - View all
Common terms and phrases
adsorbed alkaline alloy aluminium anodic applications Artificial Intelligence atoms Boiling Point Curve brazing cathodic chemical engineering chloride ion chromate composition compounds concentration containing conversion coatings Corrosion Control corrosion fatigue Corrosion of Hastelloy Corrosion rates corrosion resistance Corrosion Services crack growth current density deposits effect electrochemical electronic electroplating environments expert system films formed Hastelloy Hastelloy alloy heat exchangers increase industry inhibition inhibitor interface ion implantation iron knowledge base layer material Metallurgy methods mild steel mm/year molybdate e.g. molybdenum molybdenum blue molybdic acid NaCl NC NC nickel-base alloys oxide oxygen passive phosphate pitting corrosion plating polarization potential problems properties protection rates in parentheses reduced REVIEWS rules rust sodium molybdate soldering solution specimens stainless steel stress corrosion cracking structure substrate Sulfuric Acid Table techniques Technology temperature thickness titanium tube unimplanted water path wear resistance WEIGHT PERCENT welding zinc