Page 206
He pointed out that a critical chloride ion concentration below which no SCC might occur did not exist and that the existence of a vapour space just below the upper tube sheet of a vertical exchanger might easily lead to SCC .
He pointed out that a critical chloride ion concentration below which no SCC might occur did not exist and that the existence of a vapour space just below the upper tube sheet of a vertical exchanger might easily lead to SCC .
Page 214
( 8 ) Chloride ion concentration in cooling water Table 8 shows the SCC probability classified by chloride ion concentrations . The SCC probability increases with increasing chloride ion concentration up to 100 ppm but decreases between ...
( 8 ) Chloride ion concentration in cooling water Table 8 shows the SCC probability classified by chloride ion concentrations . The SCC probability increases with increasing chloride ion concentration up to 100 ppm but decreases between ...
Page 221
103 ALL DATA F 102 CHLORIDE CONCENTRATION ( PPM ) WITHOUT BFW 10 BAW 10 ° 0 0 300 100 200 SKIN TEMPERATURE ( ° C ) Fig . 6 . Comparison between critical lines depicted on the basis of the data classified by water quality with and ...
103 ALL DATA F 102 CHLORIDE CONCENTRATION ( PPM ) WITHOUT BFW 10 BAW 10 ° 0 0 300 100 200 SKIN TEMPERATURE ( ° C ) Fig . 6 . Comparison between critical lines depicted on the basis of the data classified by water quality with and ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the fields of Corrosion and Stress | 202 |
J Kolts J B C Wu?P E Manning and A I Asphahani | 280 |
Copyright | |
45 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic applications base chemical chloride chromate coating combination composition compounds concentration considered containing Corrosion rates corrosion resistance critical curves density deposits determined effect electrochemical elements Engineering environments example expert system factor failure field Figure film growth heat higher implanted improved increase industry inhibition inhibitor ions iron knowledge layer limited materials measurements mechanism metal methods molybdate molybdenum obtained operation oxide paint passive performance pitting plating polarization possible potential present problems properties protection published Radioactive Tracer range reduced reported REVIEWS rules rust selection Services shown shows sodium solution specimens stainless steel stress corrosion cracking structure substrate surface Table techniques Technology temperature tests tube University values various zinc